Two-dimensional materials integrated with multiferroic layers

ABSTRACT

The invention relates to heterostructures including a layer of a two-dimensional material placed on a multiferroic layer. An ordered array of differing polarization domains in the multiferroic layer produces corresponding domains having differing properties in the two-dimensional material. When the multiferroic layer is ferroelectric, the ferroelectric polarization domains in the layer produce local electric fields that penetrate the two-dimensional material. The local electric fields can influence properties of the two-dimensional material, including carrier density, transport properties, optical properties, surface chemistry, piezoelectric-induced strain, magnetic properties, and interlayer spacing. Methods for producing the heterostructures are provided. Devices incorporating the heterostructures are also provided, including tunable sensors, optical emitters, and programmable logic gates.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application claims priority to U.S. Provisional Application No. 62/424,711, filed on Nov. 21, 2016, the contents of which are incorporated herein by reference in their entirety.

TECHNICAL FIELD

This application relates generally to heterostructures including a layer of a two-dimensional material placed on a multiferroic layer. An ordered array of differing polarization domains in the multiferroic layer produces corresponding domains having differing properties in the two-dimensional material. When the multiferroic layer is ferroelectric, the ferroelectric polarization domains in the layer produce local electric fields that penetrate the two-dimensional material. The local electric fields can influence properties of the two-dimensional material, including carrier density, transport properties, optical properties, surface chemistry, piezoelectric-induced strain, magnetic properties, and interlayer spacing. Methods for producing the heterostructures are provided. Devices incorporating the heterostructures are also provided.

BACKGROUND

The conventional method for introducing an electric field and varying the carrier density in a semiconductor channel is to use an electrostatic gate consisting of a gate dielectric layer and a metal contact layer over the semiconductor transport channel. Such gates are fabricated using standard lithographic techniques, and they are normally used to apply an electric field, but their geometry is fixed once they are fabricated. The intent is to control charge flow, not determine the luminescent or chemical sensing properties. Strain is normally introduced by mechanical means.

Ferroelectric films have recently been used as the gate dielectric in transistor structures because their polarization is non-volatile (it remains after the gate voltage has been removed). A ferroelectric transistor utilizes the nonvolatile, switchable polarization field of a ferroelectric gate to control the charge carrier density in the conducting channel. This approach is actively researched as an avenue to nonvolatile transistor memory, known as ferroelectric random access memory (FeRAM).

However, the conventional methods suffer from several drawbacks. The lateral size of such a gate is determined by the limits of the lithography used to produce it, and it cannot be changed once it is fabricated. The gate is typically on the top surface, and therefore covers the active material, preventing its use as either a chemical vapor sensor or as an optical emitter. The gate requires constant power, and electric field or charge disappears once the power is removed—such gates are volatile rather than non-volatile. Finally, doping with impurity atoms is irreversible, and introduces potential defects.

SUMMARY OF THE INVENTION

The invention described herein, including the various aspects and/or embodiments thereof, meets the unmet needs of the art, as well as others, by providing heterostructures including a layer of a two-dimensional material placed on a multiferroic layer. An ordered array of differing polarization domains in the multiferroic layer produces corresponding domains having differing properties in the two-dimensional material. When the multiferroic layer is ferroelectric, the ferroelectric polarization domains in the layer produce local electric fields that penetrate the two-dimensional material. The local electric fields can influence properties of the two-dimensional material, including carrier density, transport properties, optical properties, surface chemistry, piezoelectric-induced strain, magnetic properties, and interlayer spacing. Methods for producing the heterostructures are provided. Devices incorporating the heterostructures are also provided.

In accordance with one aspect of the invention, a heterostructure includes a multiferroic material layer; and a two-dimensional material layer provided on the multiferroic material layer. The multiferroic material layer comprises an array of polarization domains in the multiferroic layer, and produces corresponding domains in the two-dimensional material.

According to another aspect of the invention, a detector includes a ferroelectric material layer; and a two-dimensional material layer provided on the ferroelectric material layer. The ferroelectric material layer includes an array of dipole domains in the ferroelectric material layer, and produces corresponding n-type and p-type domains in the two-dimensional material layer. In some aspects, the n-type and p-type domains in the two-dimensional material layer can be used to simultaneously detect electron-donating chemicals and hole-donating chemicals within same sensor. The detector of the invention enables more comprehensive detection and more accurate identification of detected molecules.

According to a further aspect of the invention, a method for forming a heterostructure includes providing a multiferroic material layer; applying a local electric field to the multiferroic material layer, forming an array of polarization domains in the multiferroic layer; and providing a two-dimensional material layer on the multiferroic material layer having an array of polarization domains therein, wherein the polarization domains produce corresponding domains in the two-dimensional material.

Other features and advantages of the present invention will become apparent to those skilled in the art upon examination of the following or upon learning by practice of the invention.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing the relative ΔG/G₀ for an n-type MoS₂ monolayer exposed to electron-donating molecules and hole-donating molecules.

FIG. 2 is a depiction of a detection device in which polarization domains in an underlying ferroelectric layer create n-type and p-type domains.

FIG. 3(a) depicts a PMMA film transfer method. FIG. 3(b) depicts a PDMS film transfer method.

FIG. 4 depicts a configuration for polarization domains, written into a 150 nm PZT/Pt/SiO₂/Si test sample using a conductive atomic force microscope (CAFM).

FIG. 5(a) is an image of a 100 nm PZT film surface poled using an atomic force microscopy (AFM) operated in the electrostatic force microscopy phase mode. FIG. 5(b) is a horizontal EFM line scan averaged left to right across the top two panels of the checkerboard of FIG. 5(a). FIG. 5(c) is a schematic cross section of the PZT film, illustrating the orientation of the polarization domains and the corresponding surface charge. FIG. 5(d) is a PL peak intensity map obtained from the WS₂ monolayer. FIG. 5(e) is a spatial map of the PL linewidth (FWHM) corresponding to the data of FIG. 5(d).

DETAILED DESCRIPTION OF EMBODIMENTS OF THE INVENTION

The invention described herein, including the various aspects and/or embodiments thereof, meets the unmet needs of the art, as well as others, by providing heterostructures including at least one layer of a two-dimensional material adjacent to a multiferroic layer. An ordered array of differing polarization domains in the multiferroic layer produces corresponding domains having differing properties in the two-dimensional material. When the multiferroic layer is ferroelectric, the ferroelectric polarization domains in the layer produce local electric fields that penetrate the two-dimensional material. The local electric fields can influence properties of the two-dimensional material, including carrier density, transport properties, optical properties, surface chemistry, piezoelectric-induced strain, magnetic properties, and interlayer spacing. Methods for producing the heterostructures are provided. Devices incorporating the heterostructures are also provided.

The invention provides ways to control and modulate the environment surrounding 2D materials on the nanometer length scale by coupling 2D materials with multiferroic materials. In some aspects of the invention, a heterostructure is provided in which one layer is comprised of one or more 2D materials (either a single monolayer, or multiple monolayers having the same or different composition), and the adjacent layer is comprised of a multiferroic material. This multiferroic material can be a ferroelectric material, where local electrostatic domains consisting of dipole ensembles produce a local electric field, modifying the dielectric environment. If the ferroelectric material is a thin film, the strength of the electric field is related to the thickness of the film. These domains can be oriented by a global applied electric field, or manipulated at the micron to nanoscale levels with an optical beam, proximal probe such as a conducting atomic force microscope tip (as illustrated in FIGS. 5(a)-5(e)), or other techniques, including optical probes.

These polarization domains in the multiferroic or ferroelectric material can directly change the properties of adjacent 2D material monolayer(s), which are strongly affected by their immediate environment due to lack of bulk screening. The dielectric screening is very low due to their two-dimensional character relative to bulk material, and the screening that would normally occur due to carriers in a three-dimensional material is largely absent. These changes in environment in turn dramatically impact the optical, electronic and mechanical properties of the 2D material. Modification of the properties of the 2D material can be accomplished, for example, by electrostatic and piezoelectric mechanisms, or by changing the layer spacing between the monolayers in a multiple-monolayer 2D material film. Properties of 2D materials and their heterostructures can be modified and controlled by variations in the local electric field induced by local dipoles in an adjacent ferroelectric layer. This effect and mechanism is distinct from an electric field applied by a standard gate terminal.

Heterostructures and Devices.

The heterostructures of the invention include a multiferroic layer adjacent to (and preferably directly in contact with) one or more two-dimensional material layers.

The two-dimensional (“2D”) materials of the invention may be used as a single monolayer, or provided as multiple monolayers. When multiple monolayers are used, preferably from 2 to 20 monolayers are provided, more preferably from 2 to 10, still more preferably from 3 to 6. The monolayers may be formed from a variety of materials, including transition metal dichalcogenides (“TMDs”), silicene, phosphorene, and graphene. The TMDs for use in the apparatus and methods of the invention have the chemical formula MX₂, where M is a transition metal, and X is a chalcogen.

Transition metals include elements from Groups 3-12 of the periodic table. The transition metals include Sc, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Ag, Cd, La, Hf, Ta, W, Re, Os, Ir, Pt, Au, Hg, Ac, Rf, Db, Sg, Bh, Hs, Mt, Ds, Rg, and Cn, as well as the lanthanide series elements (La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu), and actinide series elements (Ac, Th, Pa, U, Np, Pu, Am, Cm, Bk, Cf, Es, Fm, Md, No, Lr). Preferred transition metals for use in the apparatus and methods of the invention include Mo, W, Nb, Hf, Ta, and V, with Mo, W, Nb, and Ta being particularly preferred.

Chalcogens include the elements found in Group 16 of the periodic table. The chalcogens include O, S, Se, Te, and Po. Preferred chalcogens for use in the apparatus and methods of the invention include S, Se, and Te, with S and Se being particularly preferred.

In some aspects of the invention, preferred 2D TMD materials for use in the sensors, systems, and methods may be selected from the group consisting of MoS₂, MoSe₂, WS₂, WSe₂, VS₂, VSe₂, VTe₂, NbS₂, NbSe₂, TaS₂, TaSe₂, and combinations thereof. Additional TMD materials formed from the transition metals and chalcogens set forth above are also within the scope of the invention.

The invention also beneficially eliminates the need for impurity doping to create n- or p-type regions in a 2D TMD layer. TMD monolayers are known to be ambipolar (i.e., they can be biased to be either n- or p-type). The heterostructures of the invention incorporating ferroelectric materials having arrays of polarization domains enable the creation of n- and p-type domains within the TMD layer, without the need for impurity doping, which is very difficult to accomplish in a monolayer.

The multiferroic material can be any material that exhibits more than one primary ferroic order parameter (which include ferromagnetism, ferroelectricity, and ferroelasticity). In some aspects of the invention, the multiferroic material is a ferroelectric (FE) material, where local electrostatic domains consisting of dipole ensembles exist and produce a local electric field, modifying the dielectric environment. These local domains modify and control the optical, transport and other electronic properties of the two-dimensional material. The multiferroic materials may be selected from BiMnO₃, LaMnO₃, and BiFeO₃, and combinations thereof. Ferroelectric materials may be selected from lead zirconate titanate (PZT), barium titanate, lead titanate, lead magnesium niobate-lead titanate (PMN-PT), and combinations thereof. Composites of any of these materials may also be used.

The multiferroic layer used in the invention may be provided as a bulk substrate or thin film. When the multiferroic layer is a thin film, it may optionally be supported by a substrate material such as silica (SiO₂), silicon, SiO₂/Si, or sapphire, but the invention is not limited to any particular substrate material. For example, growth of multiferroic or ferroelectric thin films on periodically poled wafers may be preferred in some aspects of the invention, to provide laterally templated growth of layers deposited thereon. Examples of substrates that may be provided, optionally as templated substrates, are lithium niobate and strontium titanate.

The 2D material monolayers of the invention may be exfoliated, mechanically transferred, or grown directly on the multiferroic or ferroelectric material. For example, multiple methods are available to mechanically transfer TMD monolayers, such as WS₂, onto alternate substrates, such as multiferroic or ferroelectric films. The transfers may be conducted using a thin layer of a transfer material, such as a PMMA (polymethyl methacrylate), PC (polycarbonate), or PDMS (polydimethylsiloxane)/PC film. The direct integration of the multiferroic with the 2D material results in the smallest possible separation (≤1 nm) between the two, thereby maximizing the electric field resulting from the polarization domains in the ferroelectric material. There is no intervening dielectric layer, as there is in a conventional electrostatic gate contact. Because the ferroelectric dipole electric field decreases with distance R, and corresponds to approximately R⁻³, the electric field strength at the 2D layer is as large as it can be when the 2D material lies directly on top of the ferroelectric layer. This electric field penetrates the 2D material layer and modifies its properties.

Ferroelectric materials exhibit a spontaneous polarization due to internal electric dipoles which are coupled to the lattice. Typical examples include BaTiO₃, BiFeO₃, and PbTiO₃. They can be polarized in a particular direction and manner by a global applied electric field—this polarization is retained even after the electric field is removed (this is analogous to a magnetic material which exhibits a spontaneous magnetization, and the magnetization is retained in the absence of an applied magnetic field). The polarization can also be reversed by a global applied electric field, and the hysteresis depends upon factors that are both intrinsic (e.g., coupling of the internal dipoles to the lattice) and extrinsic (e.g., interfaces, sample structure and aspect ratio).

Ensembles of these dipoles form local domains within the ferroelectric material, with a net polarization oriented in a particular direction (up or down), just as magnetic domains exist in a ferromagnet. The invention beneficially provides methods for forming local domains in the heterostructures and devices, which can be oriented and manipulated on length scales ranging from microns to nanometers by application of a highly localized electric field applied, for example, using proximal probe techniques, such as through a voltage applied between the ferroelectric material surface and the tip of an atomic force microscope (AFM), which is preferably operated as a conducting atomic force microscope (CAFM). Isolated domains can be created in predetermined locations, or an ordered array of domains may be fabricated. Thus, the properties of the adjacent 2D materials can be controlled and modified with the same spatial resolution, i.e., if a 10 μm×10 μm checkerboard pattern is created in the ferroelectric material, the properties of the 2D material layer will also be modified in a 10 μm×10 μm pattern.

The heterostructures of the invention allow for writing and rewriting the polarization domains of the ferroelectric material in any order, size, spacing, or period, and at any time, in a non-destructive and reversible fashion, permitting the heterostructures to form the basis of a reconfigurable electronic system. The polarization domains may be provided in any arrangement, without limitation. Exemplary polarization domain configurations include a checkerboard pattern, or concentric shapes (including, without limitation, squares, rectangles, circles, ovals, shapes exhibiting one or more axes of symmetry, or irregular shapes). The polarization domains are non-volatile, and no refresh power is required. The heterostructures also permit a global erase function, which may be achieved when a global electric field is used to erase any domains written in the ferroelectric layer.

The heterostructures of the invention may be used in a device that is capable of operating based on modifications in carrier density, transport properties, optical properties, surface chemistry, piezoelectric-induced strain, magnetic properties, and/or interlayer spacing. The heterostructures of the invention are broadly applicable to the field of low-power electronics (e.g., for distributed autonomous systems), detectors (e.g., for chemical vapor sensors for biological agent and explosives detection, including, but not limited to, TEA (triethylamine), THF (tetrahydrofuran), DCB (dichlorobenzene), MeOH (methanol), NT (nitrotoluene), and DCP (dichloropentane)), transistors (including radio-frequency transistors), frequency-agile electronic and optical devices, diodes, electroluminescent/light-emitting devices, structures exhibiting negative differential resistance, programmable logic gates, and non-volatile transistor memory. The multiferroic structures of the invention may also be used for transduction and for detection of magnetic fields. The development of hybrid 2D/multiferroic heterostructures further provides new avenues for spin electronics (“spintronics”).

When used in devices, the heterostructures of the invention may optionally be combined with any suitable components, including, but not limited to, electronic contacts, and electromagnetic signal transmitters. Signal transmitters may optionally be used, for example, to generate a signal to indicate that the 2D material layer has interacted with an agent of interest. However, it is to be appreciated that one of the benefits of the invention is the simplified fabrication that it permits by eliminating deposition and lithography steps necessary to deposit and define dielectric layers and top metal layers, as no discrete insulating dielectric layer or top metal contact are required to introduce the local electric fields. In addition, the invention offers lateral spatial resolution that is comparable to or better than that available with existing lithographic techniques.

In one preferred application for the heterostructures of the invention, sensors are provided. The conductivity of monolayer TMDs, such as n-type MoS₂ monolayers, increases when exposed to electron-donating molecules (labeled “e”), and shows no response to hole-donating molecules (labeled “h”). See FIG. 1. The sensor devices of the invention use the polarization domains in ferroelectric materials underlying the TMD monolayer(s) to create local n- and p-type domains in the TMD monolayer(s), which beneficially permits simultaneous detection of electron- and hole-donating molecules with same detector, enabling more comprehensive detection and more positive identification. See FIG. 2.

Modifying Properties of 2D Materials.

In accordance with another aspect of the invention, the local electric field provided by dipoles in the ferroelectric material layer modifies the carrier density in the 2D monolayer(s), which strongly affects transport properties, mechanical properties, optical properties (emission or absorption), as well as surface chemistry. An ordered array of polarization domains of the ferroelectric material produces a corresponding ordered variation in carrier densities of the 2D material. A periodic array of such domains may impose a super period on the 2D layer, and a corresponding change in band structure. Lower carrier densities lead to formation of excitons, while higher carrier densities lead to formation of charged excitons, called trions. The relative populations of excitons and trions determines the optical emission spectrum of the 2D material. In this way, the heterostructures of the invention may be configured for light emission or absorption. Accordingly, devices including photo luminescent and light-emitting diodes are provided by the invention.

Varying the carrier density also impacts the way in which the surface interacts with molecules in the gas phase, and therefore controls the selectivity and responsivity of the 2D material as a chemical sensor, such as a chemical vapor sensor. The resistivity of single or few monolayer materials changes with charge transfer from surface adsorbates, and detection of changes in resistivity can be useful for sensing applications, such as chemical sensing. The change in resistivity with exposure to a given molecule depends upon whether the material is n- or p-type. The polarization domains in an adjacent ferroelectric layer therefore can control these properties. These properties may also be used in applications such as low power electronics, chemical vapor sensors, and optical devices.

In other aspects of the invention, when the 2D material layer is piezoelectric, the polarization domains in the adjacent ferroelectric layer create local strain domains in the 2D material with a spatial distribution that is directly determined by and correlated with the polarization domains. An ordered array of polarization domains produces a corresponding ordered variation in strain fields. The optical and electronic properties of the 2D materials are strongly affected by strain. Small changes in lattice constant can change the 2D layer from a direct gap to an indirect gap semiconductor, or change a non-magnetic material to a magnetic material. This aspect of the invention provides control of the magnetization, magnetic domain structure, and switching by controlling the polarization domain structure in the ferroelectric layer with an electric field. The heterostructures of the invention also provide a means to introduce strain in piezoelectric 2D materials at the nanoscale without resorting to mechanical fixtures.

In further aspects of the invention, monolayers of 2D materials may be attracted to one another by the van der Waals interaction to form bilayers, multilayered films, and bulk materials. Each monolayer can be the same material, or consist of different materials to form a novel van der Waals heterostructure. The spacing between the monolayers depends upon the strength of the van der Waals interaction, and this spacing determines the band structure and corresponding electronic and optical properties. The van der Waals interaction is the force which exists due to interactions between dipoles. Thus by placing a 2D material on a ferroelectric layer, the dipoles in the ferroelectric layer alter the binding force between adjacent monolayers of the 2D materials, change the layer spacing, and alter the optical and electronic properties. If an array of dipole domains is patterned in the ferroelectric layer, then the properties of the 2D material exhibit a corresponding spatial dependence. The heterostructures of the invention beneficially offer a way to alter, control, and even modulate the spacing between two monolayers of 2D materials. This spacing is a significant factor in determining the optical and electronic properties of the system, and is normally determined by the natural van der Waals interaction.

Methods.

The invention also provides methods for forming heterostructures, including, but not limited to, the heterostructures described herein. The methods include providing a multiferroic material layer and applying a local electric field to the multiferroic material layer in order to create one or more polarization domains in the multiferroic layer. For example, when the multiferroic material layer is a ferroelectric material layer, the polarization domains may comprise dipole domains.

The local electric field may be applied, for example, using an optical beam, a proximal probe (such as a conducting atomic force microscope tip), or other techniques including optical probes. When a conducting atomic force microscope is used, it may be operated at a bias voltage of from ±1 V to ±10 V. When the multiferroic material layer is a ferroelectric material, a positive tip voltage will result in polarization dipoles in the ferroelectric layer that point into the sample plane, and a negative charge at the surface of the ferroelectric layer. A negative tip voltage will result in polarization dipoles in the ferroelectric layer that point out of the sample plane, and a positive charge at the surface of the ferroelectric layer. An image of the poled surface may also be obtained using the atomic force microscope by operating it in EFM phase mode.

The polarization domains may be provided in any size, shape, pattern, or configuration that is desired, based on the properties or functions of the specific heterostructure being formed. The polarization domains may range from a nanometer scale (i.e., features having a width on the order of 1 nm or more) to multiple micron scale (i.e., features having a width on the order of 1 micron, 5 microns, 10 microns, or more). Polarization domains may be separated by domain walls having any desired width. In some aspects of the invention, the polarization domain wall width may be as low as from 1-10 nm, though wider domain walls are also included in the scope of the invention.

In some aspects of the invention, the local electric fields may be globally erased, for example, by exposing the entire multiferroic material layer, or the entire heterostructure, to a global electric field. Once erased, the multiferroic material layer may have new local electric fields applied. The process of globally erasing the polarization domains and providing a new configuration of polarization domains may be repeated multiple times. In other aspects of the invention, the polarization domains may be modified only in desired locations, by applying appropriate local electric fields to areas having polarization domains to be changed.

The local electric field may be applied to the multiferroic material layer prior to depositing a 2D material layer thereon, or it may be applied after the heterostructure including the multiferroic layer and 2D material layer has been formed. Regardless of the order of these steps, the polarization domains in the multiferroic material layer produce corresponding domains in the two-dimensional material layer that is provided on the multiferroic material layer. The term “corresponding domains” is used to refer to domains in a 2D material layer that is part of a heterostructure, where the domains have properties (such as those described above) that are influenced by or result from proximity to a polarization domain of a multiferroic material. These domains are typically positioned opposite to a polarization domain formed in a multiferroic material.

The 2D material layer may be applied to the multiferroic material layer using a technique selected from the group consisting of mechanical exfoliation, mechanical transfer, and growth directly on the multiferroic material layer.

The 2D material layer may be applied directly to a multiferroic material layer in some aspects of the invention. When the 2D material layer is applied to a substrate and is transferred to the multiferroic layer, the transfer may be carried out using mechanical techniques. Regardless of the material to which it is applied, the 2D material layer may be deposited by chemical vapor deposition or other deposition or growth technique to a thickness of 1 monolayer (which is about 0.7 nm thick for a TMD monolayer, but those skilled in the art will appreciate that the thickness of the monolayer will depend on the specific monolayer composition). More than one monolayer may also be applied to form the 2D material layer, either by sequential application of layers or by depositing multiple layers simultaneously.

EXAMPLES

Aspects of the invention will now be particularly described by way of example. However, it will be apparent to one skilled in the art that the specific details are not required in order to practice the invention. The following descriptions of specific embodiments of the present invention are presented for purposes of illustration and description. They are not intended to be exhaustive of or to limit the invention to the precise forms disclosed. Many modifications and variations are possible in view of the above teachings. The embodiments are shown and described in order to best explain the principles of the invention and its practical applications, to thereby enable others skilled in the art to best utilize the invention and various embodiments with various modifications as are suited to the particular use contemplated.

Example 1

One method for mechanically transferring a TMD monolayer, such as WS₂, onto a substrate, such as a ferroelectric film, includes the use of a PMMA film, as illustrated in FIG. 3(b). A sample including a layer of WS₂ on an SiO₂ substrate is coated with a thin layer of PMMA (polymethyl methacrylate) resist and cured on a hot plate at 100° C. for 10 minutes, then submerged in buffered hydrofluoric acid to etch the SiO₂, freeing the WS₂ from the growth substrate. Once fully etched, the film was rinsed in deionized H₂O, where it floated on the surface, and was then lifted from the water using the desired substrate. Optionally, adhesion of the WS₂ layer may be improved by spinning at 2000 rpm and baking at 100° C. An acetone and isopropanol soak removes the PMMA. An optical image of PMMA transferred WS₂ exhibits a uniform, clean, triangular shape, and is also shown in FIG. 3(b).

Example 2

Another method for mechanically transferring a TMD monolayer, such as WS₂, onto a substrate, such as a ferroelectric film, includes the use of a PDMS/PC film, as illustrated in FIG. 3(c). A sample including a layer of WS2 on an SiO₂ substrate is brought into contact a PDMS/PC film, then retracted. This moves the WS2 from Si/SiO₂ onto the PDMS/PC film. The PDMS/PC/WS₂ stack is then placed onto clean Si/SiO₂. The PDMS stamp is retracted, leaving the PC film on the top surface of WS₂, which is then dissolved in chloroform. An optical image following PDMS transfer is shown in FIG. 3(c).

Example 3

Polarization domains were written into a 150 nm PZT/Pt/SiO₂/Si test sample using a conductive atomic force microscope (CAFM) manufactured by Park Systems (Suwon, South Korea), in order to demonstrate that polarization domains in the ferroelectric film control photoluminescence (PL) intensity of mechanically transferred WS₂ monolayers. The sample is shown in FIG. 4.

The 6×6 micron image shown in FIG. 4 was obtained using the AFM operating in electric force microscopy imaging mode. The dark regions of the image correspond to the areas of the sample in which the AFM created dipole domains pointing up. The light regions of the image correspond to the areas of the sample in which the AFM created dipole domains pointing down. This is shown schematically in the accompanying cross section corresponding to the fiducial line drawn through the image. While the dipole domains shown here are about 500 nm in lateral dimension, domains on the scale of a few nanometers can also be successfully created and imaged.

Example 4

A large area monolayer WS₂ grown by a CVD process on a SiO₂/Si substrate in a 2 inch tube furnace. WO₃ powder and sulfur precursors were heated to 825° C. under a 100 sccm argon and 10 sccm hydrogen flow. Perylene-3,4,9,10-tetracarboxylic acid tetrapotassium salt was used as seed molecules to promote lateral growth. The monolayer nature was confirmed by Raman and PL mapping.

The WS₂ film was removed from the SiO₂/Si growth substrate and transferred onto a 100 nm thick PZT film on a conducting n-type strontium titanate wafer. Transfer was conducted using the method of Example 1. Before transfer, a metal marker grid pattern (Ti/Au) was deposited on the PZT film using either a shadow mask or photolithography technique, in order to assist in locating specific poled areas.

Polarization domains were written into the PZT film using a C-AFM (Park Systems NX-10), which was operated using dc voltages of up to ±10 V, using two types of cantilevers: Cr—Pt coated (Multi75E, Budget Sensors) and Au-coated (PPP-NCSTAu, Nanosensors) Si cantilevers. Similar results were obtained with both. A tip voltage of ±10 V direct current (dc) was applied in the contact mode, and polarization domains were written in a checkerboard pattern. Line scan densities of at least 512 lines per 10 μm were used to write the polarization domains into the PZT in a checkerboard pattern with the tip polarities shown. Dynamic contact electrostatic force microscopy was used to image the polarization state of the poled regions, at a frequency of 75-160 kHz. The total image size is 30×30 μm, and each poled square is 10×10 μm. The dashed lines are provided as a guide, and the bias voltages applied to the C-AFM tip are indicated.

An image of the poled 100 nm PZT surface was obtained using the same AFM operated in the electrostatic force microscopy phase mode, and an EFM phase image of the area is shown in FIG. 5(a).

FIG. 5(b) shows a horizontal EFM line scan averaged left to right across the top two panels of the checkerboard pattern. There is strong contrast between the squares written with opposite AFM tip polarities, indicating successful poling of the PZT film. There is little contrast between the areas of PZT that were not poled by the AFM and the squares that were intentionally poled using a +10 V tip bias, due to global poling of the entire PZT film before application of the AFM. FIG. 5(c) shows a schematic cross section of the PZT film illustrating the orientation of the polarization domains and corresponding surface charge.

A PL peak intensity map was obtained from the WS₂ monolayer over a 30×30 μm area in the sample plane, acquired from a region of the PZT that was intentionally poled by the AFM with the checkerboard pattern, as shown in FIG. 5(d). A spatial map of the PL linewidth (FWHM) corresponding to the data of FIG. 5(d) is shown in FIG. 5(e).

It will, of course, be appreciated that the above description has been given by way of example only and that modifications in detail may be made within the scope of the present invention.

Throughout this application, various patents and publications have been cited. The disclosures of these patents and publications in their entireties are hereby incorporated by reference into this application, in order to more fully describe the state of the art to which this invention pertains.

The invention is capable of modification, alteration, and equivalents in form and function, as will occur to those ordinarily skilled in the pertinent arts having the benefit of this disclosure. While the present invention has been described with respect to what are presently considered the preferred embodiments, the invention is not so limited. To the contrary, the invention is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the description provided above. 

What is claimed:
 1. A heterostructure comprising: a multiferroic material layer; and a two-dimensional material layer provided on the multiferroic material layer, wherein the multiferroic material layer comprises an array of polarization domains in the multiferroic layer, and produces corresponding domains in the two-dimensional material.
 2. The heterostructure of claim 1, wherein the multiferroic material layer is a ferroelectric material layer.
 3. The heterostructure of claim 2, wherein the ferroelectric polarization domains in the ferroelectric material layer produce local electric fields that penetrate the two-dimensional material layer.
 4. The heterostructure of claim 3, wherein the local electric fields modify properties of the corresponding domains in the two-dimensional material.
 5. The heterostructure of claim 4, wherein the properties are selected from the group consisting of carrier density, transport properties, optical properties, surface chemistry, piezoelectric-induced strain, magnetic properties, and interlayer spacing.
 6. The heterostructure of claim 3, wherein the local electric fields create local n-type and p-type domains in the two-dimensional material layer.
 7. The heterostructure of claim 1, wherein the multiferroic material layer is selected from the group consisting of BiMnO₃, LaMnO₃, and BiFeO₃, and combinations thereof.
 8. The heterostructure of claim 2, wherein the ferroelectric material layer is selected from the group consisting of lead zirconate titanate (PZT), barium titanate, lead titanate, lead magnesium niobate-lead titanate (PMN-PT), and combinations thereof
 9. The heterostructure of claim 1, wherein the two-dimensional material layer is selected from the group consisting of transition metal dichalcogenide (TMD), silicene, phosphorene, graphene, and combinations thereof.
 10. The heterostructure of claim 9, wherein the two-dimensional material layer is a TMD selected from the group consisting of MoS₂, MoSe₂, WS₂, and WSe₂.
 11. A device comprising the heterostructure of claim
 1. 12. The device of claim 11, wherein the device is selected from the group consisting of sensors, optical emitters, and programmable logic gates.
 13. A chemical sensor, comprising: a ferroelectric material layer; and an MoS₂ two-dimensional material layer provided on the ferroelectric material layer, wherein the ferroelectric material layer comprises an array of dipole domains in the ferroelectric material layer, and produces corresponding n-type and p-type domains in the MoS₂ two-dimensional material.
 14. The chemical sensor of claim 13, wherein the n-type domains in the MoS₂ two-dimensional material detect electron-donating chemicals, and the p-type domains detect hole-donating chemicals.
 15. A method for forming a heterostructure, comprising: providing a multiferroic material layer; applying a local electric field to the multiferroic material layer, forming an array of polarization domains in the multiferroic layer; providing a two-dimensional material layer on the multiferroic material layer having an array of polarization domains therein, wherein the polarization domains produce corresponding domains in the two-dimensional material.
 16. The method of claim 15, wherein the local electric field is applied by an atomic force microscope.
 17. The method of claim 15, wherein the two-dimensional material layer is provided using a technique selected from the group consisting of mechanical exfoliation, mechanical transfer, and growth on the multiferroic material layer.
 18. The method of claim 15, further comprising applying a global electric field to erase the polarization domains in the multiferroic layer.
 19. The method of claim 18, further comprising applying a local electric field to form a second array of polarization domains in the multiferroic layer.
 20. The method of claim 15, wherein the multiferroic material layer is a ferroelectric material layer, and the polarization domains comprise dipole domains. 